Synthesis of Poly isobutyl vinyl ether I graft I Poly ethylene oxide Co polymer with Pendant Methacrylate Functionality and Its Photo curing Behavior
Yazarlar (5)
Elif Sezin Devrim
İstanbul Teknik Üniversitesi, Türkiye
İstanbul Teknik Üniversitesi, Türkiye
Muhammet U. Kahveci
İstanbul Teknik Üniversitesi, Türkiye
İstanbul Teknik Üniversitesi, Türkiye
Prof. Dr. Mehmet Atilla TAŞDELEN İstanbul Teknik Üniversitesi, Türkiye
Koichi Ito
Toyohashi University of Technology, Japonya
Toyohashi University of Technology, Japonya
Öğr. Gör. Yusuf Yagci İstanbul Teknik Üniversitesi, Türkiye
| Makale Türü |
Özgün Makale
(SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale)
|
||
| Dergi Adı | Designed Monomers and Polymers (Q3) | ||
| Dergi ISSN | 1385-772X Dergi Bilgileri (2009) | ||
| Dergi Tarandığı Indeksler | SCI-Expanded | ||
| Makale Dili | İngilizce | Basım Tarihi | 01-2009 |
| Kabul Tarihi | – | Yayınlanma Tarihi | 01-01-2009 |
| Cilt / Sayı / Sayfa | 12 / 3 / 265–272 | DOI | 10.1163/156855509X436085 |
| Makale Linki | http://booksandjournals.brillonline.com/content/journals/10.1163/156855509x436085 | ||
| UAK Araştırma Alanları |
Polimer Bilimi
|
||
| Özet |
| Poly(isobutyl vinyl ether)-graft-poly(ethylene oxide) graft co-polymer with pendant methacrylate groups (PIBVE-g-PEO) was obtained by photoinitiated living cationic co-polymerization of isobutyl vinyl ether (IBVE) with α-vinyloxy-ω-methacryloyl-poly(ethylene oxide) (VE-PEO-MA) macromonomer. For this purpose, anionically prepared VE-PEO-MA hybrid macromonomer and IBVE were irradiated in the presence of diphenyl iodonium iodide and zinc iodide as photoacid generator and activator, respectively. Successful graft co-polymerization and conservation of pendant double bonds were confirmed by GPC, and 1H-NMR and FT-IR spectral analysis. The free radical photo-cross-linking behavior of the graft co-polymer was demonstrated. |
| Anahtar Kelimeler |
| Graft co-polymers | Living cationic polymerization | Macromonomer | Photo-curing | Photo-polymerization |