Self propagating High Temperature Synthesis of TiB2
Yazarlar (3)
Ahmet Turan İstanbul Teknik Üniversitesi, Türkiye
Doç. Dr. Mehmet BUĞDAYCI Yalova Üniversitesi, Türkiye
Onuralp Yucel İstanbul Teknik Üniversitesi, Türkiye
| Makale Türü |
Özgün Makale
(SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale)
|
||
| Dergi Adı | High Temperature Materials and Processes | ||
| Dergi ISSN | 0334-6455 Wos Dergi Scopus Dergi | ||
| Dergi Tarandığı Indeksler | SCI-Expanded | ||
| Makale Dili | İngilizce | Basım Tarihi | 04-2015 |
| Kabul Tarihi | – | Yayınlanma Tarihi | 14-06-2014 |
| Cilt / Sayı / Sayfa | 34 / 2 / 185–193 | DOI | 10.1515/htmp-2014-0021 |
| Makale Linki | http://www.degruyter.com/view/j/htmp.ahead-of-print/htmp-2014-0021/htmp-2014-0021.xml | ||
| Özet |
| Self-propagating high temperature synthesis (SHS) is a very important technique for the synthesis of high technology ceramics, metals and alloys. SHS parameters of TiB2 were carried out in this study. Mg stoichiometry as reductant, process atmosphere and addition of NaCl and MgSO4· 7H2O additives were investigated. HCl leaching was applied to SHS products to purify their TiB2 contents. Stoichiometrically 100% Mg addition ratio and Ar atmosphere were determined as the optimum parameters. NaCl addition was also positively affected the specific surface area values. 11.78 m2/g specific surface area value was measured for 5.0% NaCl addition ratio. |
| Anahtar Kelimeler |
| metallothermic reduction | self-propagating high temperature synthesis | titanium diboride |