Nailed-bat like halloysite nanotube filled polyamide 6,6 nanofibers by electrospinning
Yazarlar (3)
Doç. Dr. Hatice Aylin KARAHAN TOPRAKÇI
Yalova Üniversitesi, Türkiye
Doç. Dr. Ozan TOPRAKÇI
Yalova Üniversitesi, Türkiye
| Makale Türü | Özgün Makale (SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale) | ||
| Dergi Adı | Polymer-Plastics Technology and Materials (Q3) | ||
| Dergi ISSN | 2574-0881 Wos Dergi Scopus Dergi | ||
| Dergi Tarandığı Indeksler | SCI-Expanded | ||
| Makale Dili | İngilizce | Basım Tarihi | 03-2021 |
| Cilt / Sayı / Sayfa | 60 / 5 / 522–535 | DOI | 10.1080/25740881.2020.1819313 |
| Makale Linki | http://dx.doi.org/10.1080/25740881.2020.1819313 | ||
| Özet |
| The present study focuses on fabrication and characterization of halloysite nanotube (HNT) filled polyamide 6,6 nanocomposite fibers. HNTs were incorporated into the spinning solution at various concentration levels changing from 5 to 30 wt%. To understand the changes in the fiber morphology, viscosity, and conductivity of the electrospining solutions were also investigated. Depending on the filler ratio, increase in the solution viscosity was around 5–19%. However the change in solution conductivity was not significant and around 0.22–2.5 %. In addition to solution properties, morphology, structure, thermal and mechanical properties of the electrospun nanocomposite fibers were characterized. Morphological analysis showed the highly porous nanofibrous mat structure for all samples. HNT filled samples showed higher average fiber diameter than PA 6,6 fibers with the values around 105–162 nm. One … |
| Anahtar Kelimeler |
| Polymer nanocomposites | halloysite nanotubes | nanocomposite electrospun fibers |