Preparation of super HIPS via nanocomposite assemblies in the presence of toughener intercalant
Yazarlar (5)
Cüneyt Bağcıoğlu
Bogazici University, Türkiye
Bogazici University, Türkiye
Prof. Dr. Sinan ŞEN Yalova Üniversitesi, Türkiye
Öğr. Gör. Yusuf Yağcı İstanbul Teknik Üniversitesi, Türkiye
Turgut Nugay
Boğaziçi Üniversitesi, Türkiye
Boğaziçi Üniversitesi, Türkiye
Nihan Nugay
Boğaziçi Üniversitesi, Türkiye
Boğaziçi Üniversitesi, Türkiye
| Makale Türü |
Özgün Makale
(SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale)
|
||
| Dergi Adı | E Polymers (Q4) | ||
| Dergi ISSN | 1618-7229 | ||
| Dergi Tarandığı Indeksler | SCI-Expanded | ||
| Makale Dili | İngilizce | Basım Tarihi | 08-2008 |
| Kabul Tarihi | – | Yayınlanma Tarihi | 01-12-2008 |
| Cilt / Sayı / Sayfa | 8 / 1 / 1119–1130 | DOI | 10.1515/epoly.2008.8.1.1119 |
| Makale Linki | http://www.degruyter.com/view/j/epoly.2008.8.issue-1/epoly.2008.8.1.1119/epoly.2008.8.1.1119.xml | ||
| UAK Araştırma Alanları |
Polimer Bilimi ve Teknolojileri
|
||
| Özet |
| Highly toughened super high-impact polystyrene (HIPS)/organophilic montmorillonite (Org-MMT) nanocomposite was prepared by solution blending method. Organophilic modification of MMT layered silicate was achieved by using a special toughener-intercalant, quaternary ammonium salt of α-tertiary amine functionalized polybutadiene and shown by X-ray diffraction analysis. The resulting HIPS/Org-MMT nanocomposite was characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), atomic force microscopy (AFM), thermogravimetric analysis (TGA), and static and dynamic mechanical analyses. The morphological study of HIPS/Org-MMT nanocomposite showed that nanolayers were exfoliated in nanocomposite and moreover caused much more well dispersed and reduced PS occluded rubber domains. This mechanism was found to be responsible for dramatic increase in toughness of … |