Preparation of Carbon Nanotube TiO2 Mesoporous Hybrid Photoanode with Iron Pyrite FeS2 Thin Films Counter Electrodes for Dye Sensitized Solar Cell
Yazarlar (8)
Prof. Dr. Bayram KILIÇ Yalova Üniversitesi, Türkiye
Prof. Dr. Sunay TÜRKDOĞAN Yalova Üniversitesi, Türkiye
Prof. Dr. Aykut Astam Erzincan Üniversitesi, Türkiye
Oğuz Can Özer Yalova Üniversitesi, Türkiye
Mansur Aşgın Yalova Üniversitesi, Türkiye
Prof. Dr. Hülya Cebeci İstanbul Teknik Üniversitesi, Türkiye
Deniz Ürk İstanbul Teknik Üniversitesi, Türkiye
Selin Paravadılı Mucur Tubıtak Marmara Research Center, Türkiye
| Makale Türü |
Özgün Makale
(SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale)
|
||
| Dergi Adı | Scientific Reports (Q1) | ||
| Dergi ISSN | 2045-2322 Dergi Bilgileri (2016) | ||
| Dergi Tarandığı Indeksler | SCI | ||
| Makale Dili | İngilizce | Basım Tarihi | 05-2016 |
| Kabul Tarihi | 13-05-2016 | Yayınlanma Tarihi | 31-05-2016 |
| Cilt / Sayı / Sayfa | 6 / 1 / 27052–0 | DOI | 10.1038/srep27052 |
| Makale Linki | https://www.nature.com/articles/srep27052.pdf | ||
| UAK Araştırma Alanları |
Yarı İletkenler
|
||
| Özet |
| Multi-walled carbon nanotube (MWCNT)/TiO2 mesoporous networks can be employed as a new alternative photoanode in dye-sensitized solar cells (DSSCs). By using the MWCNT/TiO2 mesoporous as photoanodes in DSSC, we demonstrate that the MWCNT/TiO2 mesoporous photoanode is promising alternative to standard FTO/TiO2 mesoporous based DSSC due to larger specific surface area and high electrochemical activity. We also show that iron pyrite (FeS2) thin films can be used as an efficient counter electrode (CE), an alternative to the conventional high cost Pt based CE. We are able to synthesis FeS2 nanostructures utilizing a very cheap and easy hydrothermal growth route. MWCNT/TiO2 mesoporous based DSSCs with FeS2 CE achieved a high solar conversion efficiency of 7.27% under 100 mW cm−2 (AM 1.5G 1-Sun) simulated solar irradiance which is considerably (slightly) higher than that of A … |