Development and properties of n-octadecane / kaolinite composites as form-stabilized phase change materials for energy storage
Yazarlar (3)
Prof. Dr. Mehmet Selçuk MERT Yalova Üniversitesi, Türkiye
Prof. Dr. Hatice Hande MERT Yalova Üniversitesi, Türkiye
Müslüm Arıcı Kocaeli Üniversitesi, Türkiye
| Makale Türü | Özgün Makale (SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale) | ||
| Dergi Adı | Journal of Cleaner Production (Q1) | ||
| Dergi ISSN | 0959-6526 Wos Dergi Scopus Dergi | ||
| Dergi Tarandığı Indeksler | SCI-Expanded | ||
| Makale Dili | İngilizce | Basım Tarihi | 07-2023 |
| Kabul Tarihi | – | Yayınlanma Tarihi | 01-07-2023 |
| Cilt / Sayı / Sayfa | 410 / 1 / 137304–0 | DOI | 10.1016/j.jclepro.2023.137304 |
| Makale Linki | http://dx.doi.org/10.1016/j.jclepro.2023.137304 | ||
| Özet |
| Thermal energy storage (TES) is one of the promising options applied for obtaining energy-saving possibilities. This goal can be attained by using phase change materials (PCMs) that allow storing/releasing latent heats without losses caused by temperature differences. However, in most cases these materials need to be encapsulated for various applications, especially to prevent contamination and/or loss of substance. In this work, incorporation of a kind of an organic PCM belonging to the paraffins was performed by one step impregnation method. For this purpose, n-octadecane (n-OD) having 191.7 kJ/kg latent heat of melting and 34.2 οC peak melting temperature was used. In here, Kaolinite clay (KC), which was modified with cetyltrimethylammonium bromide in order to enhance the incorporation amount of n-OD, was utilized as the support matrices and called as m-KC. The development of form-stable … |
| Anahtar Kelimeler |
| Composite phase change material | Kaolinite | n-octadecane | Thermal energy storage | Thermal properties |
Science Direct
Development and properties of n-octadecane / kaolinite composites as form-stabilized phase change materials for energy storage
BM Sürdürülebilir Kalkınma Amaçları
| Atıf Sayıları | |
| Google Scholar | 35 |
| Scopus | 35 |
| Web of Science | 34 |